M42 Tool Steel | SKH59 | HS 2-9-1-8 | 1.3247 High Speed Steel
SAE M42 Tool Steel is high cobalt high speed steel. And High Speed Steel toughness and is mainly used for high toughness precision wear-resistant metal cold die.Moreover it also can be used for the cutting tool and the knife in the cooling.
Supply Form of M42 Tool Steel -ASTM A681 High Speed Steel
Supply Range of SAE M42 Tool Steel
M42 Steel Round Bar: diameter 1mm – 400mm
M42 Steel Plate: thickness 1 –500mm x width 200– 1400mm
M42 Steel Block: 210mm x 500-810mm
Chemical Composition of M42 Tool Steel Material
ASTM A681 | C | Si | Mn | P | S | Cr | Mo | V | w | Co |
M42/ T11342 | 1.05~1.15 | 0.15~0.65 | 0.15~0.40 | 0.030 Max | 0.030 Max | 3.50~4.25 | 9.00~10.00 | 0.95~1.35 | 1.15~1.85 | 7.75~8.75 |
DIN 17350 | C | Si | Mn | P | S | Cr | Mo | V | w | Co |
1.3247/S2-10-1-8 | 1.05~1.15 | ≤0.70 | ≤0.40 | 0.030 Max | 0.030 Max | 3.50~4.50 | 9.00~10.00 | 0.90~1.30 | 1.20~1.90 | 7.50~8.50 |
GB/T 1299 | C | Si | Mn | P | S | Cr | Mo | V | w | Co |
W2Mo9Cr4VCo8 | 1.05~1.15 | 0.15~0.65 | 0.15~0.40 | 0.030 Max | 0.030 Max | 3.50~4.25 | 9.00~10.00 | 0.95~1.35 | 1.15~1.85 | 7.75~8.75 |
JIS G4403 | C | Si | Mn | P | S | Cr | Mo | V | w | Co |
SKH59 | 1.05~1.15 | ≤0.70 | ≤0.40 | 0.030 Max | 0.030 Max | 3.50~4.50 | 9.00~10.00 | 0.90~1.30 | 1.20~1.90 | 7.50~8.50 |
M42 Tool Steel Material Equivalent and Related Speciations
USA | German | Japan | China | ISO |
ASTM A681 | DIN 17350 | JIS G4403 | GB/T 1299 | ISO 4957 |
M42 | 1.3247 | SKh59 | W2Mo9Cr4VCo8 | HS 2-9-1-8 |
SAE M42 Tool Steel Material Mechanical Properties
Hardness, Rockwell C (oil quenched on 1204°C, 5 minutes): 63 HRC.
Hardness, Rockwell C (oil quenched on 1177°C, 5 minutes): 65.5 HRC
Hardness, Rockwell C(oil quenched on 1163°C), 5 minutes: 65.8 HRC
Forged of M42 Steel metal material
At first, Pre-Heating to 650-750℃,Then heat to forged temperature. Next, Soak at 1050-1100 °C , ensure heat thorough. Then start forged, the forged temperature no low than 950℃. After forging, cool slowly .
Heat Treatment of SAE M42 Steel
- M42 HSS Steel Annealing
Firstly, Slowly heat to 870℃,then slowly Cool to 538℃(1000℉) in heat treatment furnace. Then cool in air. After annealing hardness HBS: 269 Max
- M42 tool Steel Hardening
M42 steel having very high hardenability and should be hardened by cooling in still air. The use of a salt bath or controlled atmosphere furnace is desirable to minimize decarburization, and if not available, pack hardening in spent pitch coke is suggested. Finally, the temperature employed is usually 1800°-1850°F, depending on size section.
- Quenching of HSS M42 Steel material
Quenching temperature / ℃ | salt bath furnace: 1177
Quenching temperature / ℃ | controlled atmosphere furnace: 11188
The heat preservation time/min: 5 ~ 15
Quenching medium: air cooling
- Tempering Of HSS M42 Tool Steel
Tempering temperature / ℃ : 538
After tempering hardness HRC or higher: 66
Application of Sae M42 tool Steel HSS
Suitable for manufacturing various strong cutting tools with wear-resistant, resistant to impact. Advanced punching die, screw die, the toughness and complicated shape of the punch, etc. Roll cutting tool industry: scraper, serrated knife, iron knives, drill bits, etc.
Forging industry: forging die.
Screw industry: heading forming mould, such as teeth, punch
Quality Assured of Sae M42 Steel
Quality assured by ISO 9001:2008 quality management system. Whatsmore, Our all M42 tool steel all had by SEP 1921-84 ultrasonic inspection (UT Test). Quality Grade: E/e, D/d, C/c.